ASODUR-EMB Technical Data Sheet EN 1917.pdf
2 ページ
96.1キロバイト
Download
<h1>ASODUR-EMB Technical Data Sheet EN 1917.pdf</h1> <p>SCHOMBURG GmbH & Co. KG <br />Aquafinstrasse 2–8 <br />D-32760 Detmold (Germany) <br />phone + 49-5231- 953-00 <br />fax + 49-5231- 953-108 <br />email export@schomburg.de <br />www.schomburg.com</p> <p>Technical Data Sheet</p> <p>ASODUR®-EMB</p> <p>Art.-No. 2 05790</p> <p>Epoxy resin mortar</p> <p>Tensile adhesion <br />strength: <br />> 1.5 N/mm2 <br />Thickness: ≥ 3 mm to ≤ 50 mm, for localised <br />areas of damage <br />up to 1 m2 ≤ 100 mm <br />Cleaning of tools: Thoroughly clean tools <br />immediately after use with <br />ASO-R001. <br />Packaging: 8 kg and 20 kg container <br />Components A and B are supplied in <br />the correct mixing ratios. <br />Storage: Cool and dry 18 months in <br />original unopened packaging <br />above +10° C. Storage must be <br />in accordance with the regulations <br />for the storage of material <br />hazardous to water courses.</p> <p>SCHOMBURG GmbH & Co. KG <br />Aquafinstrasse 2–8 <br />D-32760 Detmold <br />06 <br />2 05790 <br />EN 13813 <br />ASODUR-EMB <br />Resin-based screed / resin-based coating for interior rooms</p> <p>SR-B1,5-AR1-IR4 <br />Reaction to fire according to K 2010/85/EU <br />Release of corrosive substances <br />Resistance to wear <br />Tensile strength <br />Impact resistance </p> <p>E <br />SR <br />AR1 <br />≥ B1,5 <br />IR4</p> <p>• Two component. <br />• Solvent free. <br />• For interior or exterior use. <br />• highly resistant to wear</p> <p>Surface preparation: <br />The area to be treated must be: <br />• dry, firm, sound and have a good grip <br />• free from separating and adhesion inhibiting substances <br />such as dust, laitance, grease, oil, rubber marks, paint <br />residues and similar. <br />• protected from moisture ingress from the rear.</p> <p>Areas of application: <br />ASODUR-EMB is used for repairing cementitious surfaces <br />as well as for the construction of coved fillets on e.g. <br />concrete roads, ramps and industrial floors. <br />Technical Data: <br />Base: <br />2 component epoxy resin <br />Colour: grey <br />Viscosity: <br />mortar consistency <br />Density: <br />approx. 2.0 g/cm3 <br />Mix ratio: <br />100 : 3.6 parts by weight <br />Curing temperature: <br />(material/substrate): +10 °C to +30 °C <br />Pot life: <br />approx. 60 mins at +23 °C <br />Ready for use: after approx. 12 hours up to <br />max. 24 hours at +23 °C <br />Overcoat: after approx. 12 hours up to max. <br />24 hours at +23 °C <br />full service conditions after 7 days <br />Compressive strength: approx. 100 N/mm2 <br />Flexural strength: <br />approx. 50 N/mm2</p> <p>Prepare substrates with reference to <br />DIN EN 14879-1:2005, 4.2 following. <br />Dependent on the condition of the substrate to be treated, <br />use suitable mechanical preparation methods, e.g. high <br />pressure water blasting, scabbling, shot blasting, planing <br />etc, with which a textured, open surface is achieved. <br />Dependent on the particular substrate, the following <br />criteria are also to be fulfilled: <br />Cementitious substrates: <br />• Concrete quality: <br />• Screed quality: <br />• Age: </p> <p>1/2</p> <p>min. C20/25 <br />min. CT-C25-F4 <br />min. 28 days</p> <p>19/17</p> <p>Important advice: <br />• Higher temperatures shorten the pot life. Lower <br />temperatures lengthen the pot life and curing time. <br />Material consumption is also increased at lower <br />temperatures. <br />• Applications that are not clearly explained in this <br />technical data sheet may only be carried out after <br />consultation with and written confirmation from the <br />technical services department of SCHOMBURG. <br />• Waste code: liquid product residues: EAK O8 01 11 <br />pigment and lacquer waste that contains organic <br />solvents or other harmful materials.</p> <p>• Tensile adhesion strength: >1,5 N/mm2 <br />• Residual moisture: < 4 % (carbide hygrometer <br />method) <br />Product preparation: <br />Component A (mortar) and component B (hardener: <br />inside) are delivered in a complimentary mix ratio. <br />Tip component B into component A. Ensure that the <br />hardener drains completely from the container. Mixing <br />of the components is to be carried out with a suitable <br />mixer at approx. 300 rpm (e.g. drill with paddle). It is <br />important to stir from the sides and the bottom to ensure <br />that the hardener is evenly dispersed. Stir until the mix is <br />homogenous. Mix time approx. 5 minutes. The material <br />temperature should be approx. +15° C during the mix <br />process. Do not use the mixed material directly from the <br />delivered packaging! Decant the mass into a clean mix <br />bucket and thoroughly mix through once again. Use a <br />forced paddle mixer (e.g. Colormatic, Zyklos or Uez) for <br />larger projects.</p> <p>Please observe a valid EU safety data sheet. <br />GISCODE: RE1</p> <p>Method of application / consumption: <br />1. Surface preparation – see above <br />2. Prime the area to be treated: <br />Apply ASODUR-GBM in one coat with a roller. <br />Consumption: approx. 300–500 g/m2 <br />2.1 Repair of damaged or defective areas in concrete <br />and screeds: <br />Trowel ASODUR-EMB into the priming coat of <br />ASODUR-GBM, whilst still wet, then subsequently <br />compact by rubbing. <br />Consumption: approx. 1900 g/m2/mm thickness <br />3. Production of coved fillets: <br />Using ASODUR-EMB, wet in wet, form the coved <br />fillet area over the primer. Radius: approx. 3–5 cm <br />Consumption: approx. 1800 g/m (with a coved fillet <br />radius of approx. 5 cm)</p> <p>The rights of the buyer with regard to the quality of our materials are based on our terms and conditions of sale and delivery. Our technical advice team will be happy to advise you in the case <br />of requirements that exceed the scope of the application described here. In order to be binding, a legally binding written confirmation is required. The product description does not release the <br />user from a duty of care. Lay a test area in the event of uncertainty. This version becomes invalid in the event of a new version being issued. <br />2/2</p> <p>CJ/CoS/TM</p> <p>19/17</p>
