ASODUR-IH Technical Data Sheet EN 3119.pdf
2 หน้า
79 กิโลไบต์
Download
<h1>ASODUR-IH Technical Data Sheet EN 3119.pdf</h1> <p>SCHOMBURG GmbH & Co. KG <br />Aquafinstrasse 2–8 <br />D-32760 Detmold (Germany) <br />phone + 49-5231- 953-00 <br />fax + 49-5231- 953-108 <br />email export@schomburg.de <br />www.schomburg.com</p> <p>ASODUR®-IH <br />Injection resin</p> <p>Technical data sheet</p> <p>INDUCRET®-VK-Injekt </p> <p>• solvent-free <br />• transparent <br />• two component <br />• resistant to alkaline solutions, diluted acids, salt <br />solutions, fuels and minerals and to freeze-thaw <br />changes <br />Areas of use: <br />ASODUR-IH is used for the force-locking bonding of <br />cracks and joints in concrete and concrete components. <br />Not suitable for statically relevant areas. <br />Technical data: <br />Basis: <br />2-comp. epoxy resin <br />Standard colour: <br />transparent <br />Viscosity*: <br />approx. 380 mPas <br />Density*: <br />approx. 1.06 g/cm³ <br />Mix ratio: <br />2 : 1 parts by weight <br />Ambient and substrate <br />temperatures: min. +8 °C <br />max. +35 °C <br />at max. 80 % rel. humidity <br />Application time: approx. 60 min. at +10 °C <br />approx. 45 min. at +20 °C <br />approx. 12 min. at +30 °C <br />Overcoat*: <br />after approx. 16 to max. 24 hours. <br />Easily withstands*: after approx. 48 hours. <br />Fully cured*: <br />after approx. 7 days <br />Compressive strength: approx. 79 N/mm² <br />Bending tensile <br />strength: <br />approx. 33 N/mm² <br />Tensile adhesion <br />strength: <br />≥ 1.5 N/mm² <br />Shore D hardness: approx. 75 <br />Water absorption: max. 1.5 mixed % <br />* at +23 °C and 50 % rel. humidity</p> <p>Art. no. 2 05769</p> <p>Packaging: 1 and 3 kg containers <br />Component A and component B are <br />in the predetermined mix ratio. <br />Storage: Frost-free, cool and dry, ≥ +10 °C to <br />+25 °C, 18 months in the original <br />unopened container, use opened <br />container promptly <br />Substrate: <br />The following criteria must be fulfilled: <br />Cement-based surfaces <br />• Quality of concrete: min. C20/25 <br />• Quality of screeds: min. EN 13813 CT-C35-F5 <br />Tensile adhesion <br />strength: <br />≥1.5 N/mm2 <br />Age: <br />min. 28 days <br />• Quality of the plaster: min. P IIIa/P IIIb <br />Tensile adhesion <br />strength: <br />approx. 0.8 N/mm2 <br />• Moisture content: <br />Immediately after use, clean tools <br />meticulously with ASO-R001.</p> <p>1/2</p> <p>31/19</p> <p>Method of application/Consumption: <br />1. Drill holes into existing cracks (crack width approx. <br />0.2 mm) at a distance of approx. 20 cm. <br />2. Clear any drilling debris in the drilled holes using <br />oil-free compressed air. <br />3. Insert the injection packer. <br />4. Seal the packer and crack zone on the surface with <br />ASODUR-EK98. <br />Strip width: <br />approx. 15 cm <br />Consumption: <br />approx. 300 g/m <br />5. A <br /> fter the crack insulation has cured, press in the <br />thoroughly mixed ASODUR-IH using a pressing device. <br />Consumption: <br />approx. 1000 g/l <br />6. A <br /> fter the injection resin has cured, remove the injection <br />packer, if relevant, and plug the boreholes flush with <br />the surface using ASOCRET-M30.</p> <p>• The indicated consumption quantities are calculated <br />values without additions for surface roughness and <br />absorbency, level compensation, and residual material <br />in the container. We recommend a calculated safety <br />addition of 10 % on top of the calculated consumption <br />quantities. <br />• Applications that have not been clearly mentioned <br />in this technical data sheet may only be carried <br />out after the technical service department of <br />SCHOMBURG GmbH has been consulted, and after <br />the said department has approved of such a course of <br />action in writing. <br />• Hardened product leftovers can be disposed of in <br />accordance with disposal code AVV 150106. <br />Please observe valid EU safety data sheets! <br />GISCODE: RE 1</p> <p>Notes: <br />•S <br /> CHOMBURG products are normally delivered in <br />working packs, i.e. in matched and predetermined mix <br />ratios. For deliveries in large packs, partial quantities <br />must be weighed out using a scale. Always stir up <br />the filled components thoroughly and only then mix <br />them with the second component. This takes place using <br />a suitable stirrer, e.g. Polyplan/a round-plate mixing <br />machine or equivalent. To avoid mixing errors, the <br />material is transferred to a clean container and mixed <br />again. The mixing speed should be approx. 300 rpm. <br />Ensure that air is not mixed in. The temperature of <br />the components should be minimum +15 °C. This also <br />applies to any filler materials that should be mixed in, <br />e.g. sand. Mixing in filler materials should take placed <br />after the liquid components have been mixed. <br />• Higher temperatures shorten the application time. <br />Lower temperatures increase the application and <br />hardening times. The rate at which material is <br />consumed also increases at lower temperatures.</p> <p>The rights of the buyer with regard to the quality of our materials are based on our terms and conditions of sale and delivery. Our technical advice team will be happy to advise you in <br />the case of requirements that exceed the scope of the application described here. In order to be binding, a legally binding written confirmation is required. The product description does not <br />release the user from a duty of care. Lay a test area in the event of uncertainty. This version becomes invalid in the event of a new version being issued. <br />2/2</p> <p>CJ/GA/KK/tet/LiB</p> <p>31/19</p>
