AQUAFIN-1K-PREMIUM Technical Data Sheet EN 3419.pdf
5 ទំព័រ
183 KB
Download
<h1>AQUAFIN-1K-PREMIUM Technical Data Sheet EN 3419.pdf</h1> <p>SCHOMBURG GmbH & Co. KG <br />Aquafinstrasse 2–8 <br />D-32760 Detmold (Germany) <br />phone + 49-5231- 953-00 <br />fax + 49-5231- 953-108 <br />email export@schomburg.de <br />www.schomburg.com</p> <p>Technical Data Sheet</p> <p>AQUAFIN®-1K-PREMIUM </p> <p>Art.-No. 2 04609</p> <p>1 component flexible waterproof slurry <br />ready to receive finishes early <br />ASO-Joint-Tape system, was tested in accordance with the <br />testing principles for waterproofing in conjunction with tiles <br />and paving slabs. <br />Also available as bonded waterproofing for the water <br />impact classes W0-I to W3-I, without chemical influence <br />in accordance with DIN 18534. <br />AQUAFIN-1K-PREMIUM is suitable for indoor use in <br />accordance with the evaluation scheme of the AgBB <br />(committee for health-related evaluation of building <br />products) and the “French VOC regulation” (French <br />VOC classification regulation and KMR emissions <br />regulation). AQUAFIN-1K-PREMIUM is very low emission <br />in accordance with GEV-EMICODE, which normally <br />results in positive evaluations within the scope of building <br />certification systems in accordance with DGNB, LEED, <br />BREEAM, HQE. Maximum quality level 4, lines 7 and 8 <br />in accordance with DGNB criteria “ENV 1.2 Risks to the <br />local environment”.</p> <p>v er</p> <p>KIWA GmbH <br />Polymer Institut</p> <p>y lo</p> <p>io n</p> <p>P11140-1/17-491</p> <p>w e m is</p> <p>s</p> <p>• 1 component <br />• Rapid hardening <br />• Tiles can be fixed after <br />only 3–4 hours <br />• Very easy to trowel and smooth off <br />• Easy and economic application <br />• Can be brushed, trowelled or <br />sprayed with suitable equipment <br />• Flexible and crack bridging <br />• Very low emission EC1 plus in accordance <br />with GEV-EMICODE <br />• Vapour permeable, resistant to frost, UV and ageing <br />• For interior and exterior use</p> <p>Technical Data: <br />Basis: </p> <p>Factory produced mortar, <br />polymer-mortar combination <br />Pot life*: <br />approx. 60 minutes <br />Testing: General technical certification <br />for liquid applied waterproofing <br />materials in combination with tiles <br />and slabs, KIWA GmbH Polymer <br />Institut P11140-1/17-491 <br />Report on classification of fire <br />performance No. 230009166-4 <br />Reaction to fire to <br />DIN EN13501-1: <br />E <br />Substrate/application <br />temperature: <br />+5 °C to +30 °C <br />Tensile adhesion strength <br />to DIN EN 1542: <br />> 0.5 N/mm2 after 28 days <br />Tear resistance*, <br />to DIN 53504: <br />> 0.4 N/mm2 <br />Elongation at break*, <br />to DIN 53504: <br />> 8 %</p> <p>Areas of application: <br />Bonded waterproof membrane in combination with tiled <br />finishes: for an assured and economical waterproof <br />membrane beneath tiles where impermeability to water <br />in long term to permanent exposure is required, e.g. in <br />bathrooms and kitchens in living areas, private and public <br />washroom facilities as well as swimming pool surrounds. <br />Perimeter, connecting and bay sizing joints are to be <br />reinforced with the incorporation of ASO-Joint-Tape-2000, <br />ASO-Joint-Tape-2000-S or ASO-DB-Standard. <br />AQUAFIN-1K-PREMIUM is suitable for wet duty exposure <br />class A in accordance with Building Authorities test criteria <br />for regulated areas PG-AIV-F and for wet duty exposure <br />classes A0 and B0 in accordance with the ZDB technical <br />sheet “Bonded waterproof membranes“. <br />The watertightness in the installed state, including the</p> <p>1/5</p> <p>34/19</p> <p>Crack bridging* <br />to DIN 28052-6 <br />(PG MDS), <br />0.4 mm crack, <br />maintained 24h: <br />passed <br />Waterproof <br />performance of <br />assembly to PG AIV, <br />(0.2 m WS): <br />passed <br />Water vapour <br />resistance factor µ: approx. 2,300 <br />Sd value at 2 mm <br />dry film thickness: <br />approx. 4.6 m <br />Consumption**: approx. 1.25 kg powder per <br />m²/ mm dry film thickness <br />Bonded waterproof <br />membrane with tiles: approx. 2.2 mm wet film thickness <br />giving approx. 2 mm dry <br />Full service conditions: - ready for tiles after approx. <br />3–4 hours <br /> <br />-w <br /> ater exposure after approx. <br />7 days <br />Packaging: <br />15 kg bag</p> <p>System components</p> <p>Storage: cool and dry, 9 month, in the original <br />unopened containers. Use opened <br />packaging promptly. <br />Cleaning: Clean tools with water whilst product is <br />still fresh. Soften dried on material with <br />ASO-R001 and wash off. <br />* at +23 °C and 60 % relative humidity <br />** Possible additional consumption in case of uneven substrates and where <br />manual variations must be considered. In accordance with DIN 18534, a <br />thickness supplement of at least 25 % should be included. <br />The stated data may be extended or shortened as a consequence of project <br />and weather conditions. Higher temperatures and lower humidity shorten the <br />drying time, lower temperatures and higher humidity extend the drying time.</p> <p>2/5</p> <p>Wet duty <br />exposure class <br />A, A0</p> <p>Wet duty <br />exposure class <br />B0</p> <p>AQUAFIN-1K-PREMIUM</p> <p>×</p> <p>×</p> <p>ASO-Unigrund-K</p> <p>×</p> <p>×</p> <p>ASO-Unigrund-GE</p> <p>×</p> <p>×</p> <p>ASO-Unigrund-S</p> <p>×</p> <p>ASO-DB-Standard</p> <p>×</p> <p>ASO-Joint-Tape-2000</p> <p>×</p> <p>×</p> <p>ASO-Joint-Tape-2000 S</p> <p>×</p> <p>×</p> <p>ASO-Joint-Tape-Sanitary</p> <p>×</p> <p>×</p> <p>ASO-Joint-Tape-2000-Corners, <br />(90°, interior/exterior)</p> <p>×</p> <p>×</p> <p>ASO-Joint-Tape-2000-S-Corners, <br />(90°, interior/exterior)</p> <p>×</p> <p>×</p> <p>ASO-Joint-Tape-2000-T-Piece, <br />-Cross-Piece</p> <p>×</p> <p>×</p> <p>ASO-Joint-Sleeve-Floor/ -Wall</p> <p>×</p> <p>×</p> <p>UNIFIX-S3</p> <p>×</p> <p>×</p> <p>LIGHTFLEX</p> <p>×</p> <p>MONOFLEX-white</p> <p>×</p> <p>MONOFLEX-white hardened with <br />UNIFLEX-F at a mass ratio of 3:1</p> <p>×</p> <p>MONOFLEX</p> <p>×</p> <p>MONOFLEX-XL</p> <p>×</p> <p>MONOFLEX-FB</p> <p>×</p> <p>ASODUR-EK98-Wall/Floor</p> <p>×</p> <p>×</p> <p>ASODUR DESIGN</p> <p>×</p> <p>×</p> <p>SOLOFLEX</p> <p>×</p> <p>SOLOFLEX-fast</p> <p>×</p> <p>AK7P</p> <p>×</p> <p>CRISTALLIT-FLEX</p> <p>×</p> <p>CRISTALLIT-MULTI-FLEX</p> <p>×</p> <p>UNIFIX-S3-FAST</p> <p>×</p> <p>×</p> <p>×</p> <p>34/19</p> <p>Substrate preparation: <br />Suitable surfaces are all flat, load-bearing surfaces that <br />can be covered with tiles and slabs and that are suitable <br />for the installation of waterproofing in combination with <br />tiled finishes. Furthermore, the suitability of the substrate <br />must be given in the corresponding wear class / water <br />impact class (see ZDB leaflet [*1]/ DIN 18534). <br />Suitable substrates are e.g. dense concrete, render P II <br />and III, fully pointed masonry work, cement-based screed, <br />moisture resistance plasterboard and gypsum fibre <br />board. Open textured substrates such as cast concrete <br />blocks, heavy concrete blocks and masonry work are <br />to be rendered with a cement-based mortar or suitable <br />smoothing compound e.g. SOLOCRET-50.</p> <p>Ensure adequate falls, in the direction of drainage, are <br />formed in areas exposed to water. <br />Floor drains should have a thin-bed flange with a minimum <br />circumferential width of 5 cm to accommodate the <br />ASO-Joint-Sleeve and be composed of a material suitable <br />for bonding to e.g. stainless steel, bronze, PVCU. <br />Heated screeds must be commissioned prior to the <br />installation of tiled flooring in accordance with recognized <br />technical regulations. The readiness of a substrate to <br />receive tiled finishes is to be determined through moisture <br />measurements with a carbide hygrometer (CM device). <br />The CM moisture content may not exceed: <br />• CT ≤ 2.0 CM% for screeds on insulation or separating <br />layers <br />• CA without underfloor heating ≤ 0.5 CM% <br />• CA with underfloor heating ≤ 0.3 CM% <br />The CM measurements are to be carried out to the <br />current FBH-AD work instructions from the technical <br />information “Coordination of cut out points with heated <br />floor constructions.”</p> <p>The substrate must be load-bearing, adequately flat to <br />DIN 18202, free from penetrating cracks and be free <br />from separating substances such as e.g. oil, paint, <br />laitance and loose parts. <br />The substrate must have a largely closed surface texture <br />and exhibit surface properties and strength commensurate <br />with its type. DIN 18157, part 1or DIN 18534 is <br />mandatory with regard to substrate, substrate preparation <br />and application. Separating cracks are to be highlighted <br />and, as necessary, adhesively sealed beforehand with <br />e.g. ASODUR-K900.</p> <p>Calcium sulphate screeds can be accepted in wear class <br />A0 or water impact classes W0-I and W1-I with indirect <br />exposure, must be sanded, vacuumed and, like all calcium <br />sulphate-bonded substrates, primed with ASO-Unigrund.</p> <p>Renders to DIN EN 998-1 must have a minimum <br />compressive strength of 2.5 N/mm² to be suitable for <br />tiling and for the relevant wet duty classification.</p> <p>Product application: <br />Place approx. 3.8–4.1 litres of water in a clean mixing <br />bucket and stir with the powder to a homogenous <br />consistency. With a mechanical drill mixer (approx. <br />500–700 rpm), a mixing time of approx. 2–3 minutes <br />is necessary. Apply AQUAFIN-1K-PREMIUM by spray, <br />brush or trowel techniques in a minimum of two coats. <br />Further coats can be applied when the previous coat <br />will not become damaged during application of the next <br />coat. Apply coats to a maximum of 2.5 mm in a single <br />operation as greater thicknesses may result in cracks <br />within the coating.</p> <p>Pre-wet the substrate so that at the time <br />AQUAFIN-1K-PREMIUM is applied, it is matt damp. <br />Prime very absorbent and slightly sandy substrates with <br />ASO-Unigrund. Prevent height differences within the <br />substrate and exclude moisture migration from the rear. <br />Even out irregularities appropriately before using <br />AQUAFIN-1K-PREMIUM. Levelling may be carried <br />out with e.g. SOLOPLAN-30-PLUS, SOLOCRET-15 or <br />SOLOCRET-50.</p> <p>3/5</p> <p>34/19</p> <p>Advice: <br />• Protect areas not being treated during the application <br />of AQUAFIN-1K-PREMIUM! <br />• Avoid dropping below the dew point (condensation) <br />during the application and drying phases on the <br />substrate and AQUAFIN-1K-PREMIUM. <br />• Allow for extended drying times in rooms with low <br />temperatures, high humidity and inadequate ventilation. <br />Direct heating in such rooms for drying purposes is not <br />suitable. <br />• Work against the direction of the sun in strong sunlight, <br />work in the shade. <br />• During the curing process the waterproof membrane <br />may not come into contact with water. Water <br />penetrating from the rear may be lead to delamination <br />in frost. <br />• Where there is moisture penetration from the rear, it <br />is necessary to pre-waterproof with AQUAFIN-1K. <br />Dependent on the water pressure, one or more coats <br />may be needed. In certain projects pre-waterproofing <br />can also be carried out with ASODUR-SG2/-SG2-thix. <br />• Direct contact with metals such as copper, zinc and <br />aluminium is to be prevented by a pore sealing primer. <br />A pore sealing primer can be produced using two <br />coats of ASODUR-GBM. Liberally apply the first coat <br />to substrate cleaned with Aceton. Once this coat has <br />reacted sufficiently so that it can no longer be disturbed <br />(approx. 3–6 hours), brush apply a second coat of <br />ASODUR-GBM and broadcast with 0.5–1.0 mm <br />quartz sand. Consumption approx. 800–1000 g/m2 <br />ASODUR-GBM. <br />• To waterproof PVC, gunmetal and stainless steel <br />flanges, abrade the flange, clean and degrease, <br />apply AQUAFIN-1K-PREMIUM and the <br />ASO-Joint-Sleeve-floor without voids or folds and <br />seamlessly connect with the membrane used on the rest <br />of the area. <br />• Heed the relevant current regulations. E.g. <br />DIN 18195 <br />DIN 18157 <br />DIN 18352</p> <p>Suitable joint tapes and pre-formed pieces are listed <br />under “Technical data/system components”. <br />Bond the joint tape or pre-formed piece with <br />AQUAFIN-1K-PREMIUM and subsequently seamlessly <br />incorporate within the surface applied membrane and <br />overcoat so that migration around the rear is prevented. <br />See also technical description 3.1.5 <br />1. Prepare the substrate in accordance with the <br />requirements for each substrate. <br />2. Pre-wet the substrate so that at the time <br />AQUAFIN-1K-PREMIUM is applied, it is matt damp. <br />Prime very absorbent and slightly sandy substrates <br />with ASO-Unigrund, allow the primer to dry before <br />continuing with other work steps. <br />3. Apply AQUAFIN-1K-PREMIUM with a plasterer’s <br />trowel, paint brush or suitable spray equipment. An <br />even coat is achieved using a 4 to 6 mm notched <br />trowel followed by smoothing. Overcoat any missed <br />areas. At least 2 coats are necessary. The previous coat <br />must have dried before the next coat is applied. <br />4. To form waterproof movement and connecting joints, <br />incorporate the ASO-Joint-Tape-System. <br />Using a 4–6 mm notched trowel, apply <br />AQUAFIN-1K-PREMIUM to both sides of the joint to be <br />bridged to a min. 2 cm wider than the joint tape. Lay the <br />ASO-Joint-Tape-System into the wet coat and thoroughly <br />press into the waterproof coating with a trowel or <br />pressure roller ensuring no voids or folds. Ensure full <br />bedding and wetting out as far as possible. Bond in <br />such a way as to prevent water migration around the <br />back of the ASO-Joint-Tape-System. The Joint Tape <br />system is laid in a loop in the movement joint. Joint-Tape <br />edges are to overlapped by a min. of 5 to 10 cm and <br />fully bonded, without voids or folds, with <br />AQUAFIN-1K-PREMIUM, then overcoated. <br />5. Tiling in thin-bed adhesives is carried out with a polymer <br />modified adhesive listed in “Technical data/ system <br />components”.</p> <p>4/5</p> <p>34/19</p> <p> <br /> <br /> <br /> <br /> </p> <p>DIN 18534 <br />DIN 18560 <br />DIN EN 13813 <br />DIN 1055 <br />The BEB information sheets, distributed by the <br />Bundesverband Estrich und Belag e.V. <br />The technical information “coordination of cut out points <br />in heated floor constructions”. <br />The ZDB information sheets, distributed by the <br />professional association of the German tile industry: <br />[*1] „Bonded waterproof membranes”“ <br />[*3] „Movement joints in wall and floor tile finishes” <br />[*5] „Ceramic tiles, natural stone and cementbound composite slabs on cement-based floor <br />constructions with insulation” <br />[*6] “Ceramic tiles, natural stone and cement bound <br />composite slabs on heated cement-based floor <br />constructions” <br />[*7] “Finishes in exterior areas”</p> <p>Please use a current valid EU Safety data sheet. <br />GISCODE: ZP1</p> <p>Information about the emission level of volatile compounds in indoor <br />air, which pose a health risk by inhalation, on a scale from class A+ <br />(very low emissions) to C (high emissions).</p> <p>The rights of the buyer with regard to the quality of our materials are based on our terms and conditions of sale and delivery. Our technical advice team will be happy to advise you in the case <br />of requirements that exceed the scope of the application described here. In order to be binding, a legally binding written confirmation is required. The product description does not release the <br />user from a duty of care. Lay a test area in the event of uncertainty. This version becomes invalid in the event of a new version being issued. <br />5/5</p> <p>WKD/CoS/TET/KKa</p> <p>34/19</p>