SANIFLEX Technical Data Sheet EN 0418.pdf
4 စာမျက်နှာများ
184 KB
Download
<h1>SANIFLEX Technical Data Sheet EN 0418.pdf</h1> <p>SCHOMBURG GmbH & Co. KG <br />Aquafinstrasse 2–8 <br />D-32760 Detmold (Germany) <br />phone + 49-5231- 953-00 <br />fax + 49-5231- 953-108 <br />email export@schomburg.de <br />www.schomburg.com</p> <p>Technical Data Sheet</p> <p>SANIFLEX</p> <p>Art.-No. 2 05004 <br />Waterproof membrane - brush, roller or trowel applied</p> <p>with GEV-EMICODE, which as a rule leads to positive <br />evaluation within the scope of building certification systems <br />in accordance with DGNB, LEED, BREEAM, HQE. Highest <br />quality level 4, rows 2,3,9 in accordance with the DGNB <br />criterion “ENV 1.2 Local environmental impact“.</p> <p>SCHOMBURG <br />GmbH & Co. KG <br />Detmold</p> <p>v er</p> <p>KIWA MPA <br />Bautest GmbH</p> <p>y lo</p> <p>io n</p> <p>P 11140-3/17-493</p> <p>w e m is</p> <p>s</p> <p>Technical Data: <br />Basis: <br />with carbonate fillers <br />Packaging: <br /> </p> <p>solvent free polymer dispersion <br />· 5, 12 and 20 kg packs in the <br />colour ochre <br />· 5 and 20 kg packs in the <br />colour grey <br />approx. 1.4 g/cm3 <br />approx. 60 mins</p> <p>Density: <br />Pot life*): <br />Application/ <br />substrate temp: <br />+5 °C to +30 °C <br />Reaction to fire according <br />to DIN EN13501-1: <br />E <br />Crack-bridging based on <br />DIN 28052-6, 0.4 mm crack, <br />maintained 24 hours: <br />passed <br />Sd value: <br />approx. 2 m <br />Testing: General technical <br />certificate for liquid applied <br />waterproofing materials in <br />combination with tiles, Bautest <br />Dresden GmbH <br />P 11140-3/17-493 <br />Emissions testing to AgBB <br />scheme, GEV-test method, <br />French and Belgian VOC <br />by-law CSTB tested (Avis <br />Techniques 13/13-1197) <br />Material consumption/ <br />minimum dry film <br />thickness: 1.2 kg/m2/approx. 0.5 mm</p> <p>• ready-to-use <br />• very low emissions <br />• solvent-free <br />• brush, roller or trowel applied <br />• vapour permeable <br />• fast drying <br />• elastic and impermeable to water <br />• for interior use <br />Areas of application: <br />Seamless and jointless waterproofing beneath tiles in wet <br />duty areas where impermeability to water is required such <br />as e.g. in domestic bathrooms and kitchens, private and <br />commercial washrooms. <br />SANIFLEX is suitable for walls in wet duty class A in <br />accordance with general technical test criteria and wet <br />duty class A0 in accordance with the ZDB data sheet <br />“Bonded waterproof membranes”. Reinforce wall/floor <br />junctions by incorporating ASO-Joint-Tape-2000 or <br />ASO-Joint-Tape-Standard into the elastic waterproof <br />membrane. <br />SANIFLEX is suitable for use in interior rooms in <br />accordance with the AgBB evaluation scheme (Committee <br />for Health-related Evaluation of Building Products) and the <br />French VOC by-law. Very low emissions in accordance</p> <p>Dry film thickness, greater material consumption on uneven substrates is not taken <br />into account.</p> <p>1/4</p> <p>04/18</p> <p>System components</p> <p>Ready for use*): foot traffic after approx. 1 day, <br />ready to install tiles after approx. 1 day <br />*)</p> <p>at +23 °C and 50 % relative humidity</p> <p>Storage: frost free, 15 months in the original <br />unopened containers. Use opened <br />packaging promptly. <br />Cleaning: Clean tools with water whilst product is <br />still fresh. Soften dried on material with <br />ASO-R003 and wash off. <br />Substrate preparation: <br />All flat, load-bearing surfaces, which can take tiles and <br />bonded waterproof membranes are suitable. Furthermore <br />the suitability of the substrate in the appropriate wet duty <br />class must be given (refer to ZDB data sheet [*1]). <br />The substrate must be load-bearing, adequately flat <br />to DIN 18202, free from penetrating cracks and be <br />free from separating substances such as e.g. oil, paint, <br />laitance layers and loose areas. The substrate must have <br />a largely closed surface and exhibit a surface condition <br />and strength commensurate with its type. DIN 18157, <br />part 1 is mandatory for substrate, substrate preparation <br />and product application. Separating cracks are to be <br />technically noted and as necessary adhesively sealed <br />beforehand e.g. with ASODUR-K900. <br />Plasters/renders to DIN EN 998-1, of strength classes <br />CS I to CS IV must have a minimum compressive strength <br />of 2.5 N/mm2 and be suitable for installing tiles in the <br />relevant wet duty class.</p> <p>Exposure classes <br />A, A0</p> <p>SANIFLEX</p> <p>×</p> <p>ASO-Unigrund-K</p> <p>×</p> <p>ASO-Unigrund-GE</p> <p>×</p> <p>ASO-Unigrund-S</p> <p>×</p> <p>ASO-Unigrund-D</p> <p>×</p> <p>ASO-DB-Standard</p> <p>×</p> <p>ASO-Joint-Tape-2000</p> <p>×</p> <p>ASO-Joint-Tape-2000-S</p> <p>×</p> <p>ASO-Joint-Tape-2000-Sanitary</p> <p>x</p> <p>ASO-Joint-Tape-2000-Corners, <br />(90°, internal/external)</p> <p>×</p> <p>ASO-Joint-Tape-2000-S-Corners, <br />(90°, internal/external)</p> <p>×</p> <p>ASO-Joint-Tape-2000-T-pieces, cross pieces</p> <p>×</p> <p>ASO-Joint-Sleeve-Floor/Wall</p> <p>×</p> <p>UNIFIX-S3</p> <p>×</p> <p>UNIFIX-2K</p> <p>×</p> <p>UNIFIX-2K/6</p> <p>×</p> <p>LIGHTFLEX</p> <p>×</p> <p>MONOFLEX-XL</p> <p>×</p> <p>ASODUR-EK98-Wall/-Floor</p> <p>×</p> <p>ASODUR-DESIGN</p> <p>×</p> <p>SOLOFLEX</p> <p>×</p> <p>AK7P</p> <p>×</p> <p>CRISTALLIT-FLEX</p> <p>×</p> <p>SOLOFLEX-white modified with UNIFLEX-B</p> <p>×</p> <p>CRISTALLIT-MULTI-FLEX</p> <p>×</p> <p>UNIFIX-S3-FAST</p> <p>×</p> <p>Level out irregularities appropriately before using <br />SANIFLEX. Levelling can be carried out e.g. with <br />the levelling compounds SOLOPLAN-30-PLUS, <br />SOLOCRET-50 or SOLOCRET-15.</p> <p>Prime absorbent and insignificantly sanded substrates with <br />ASO-Unigrund-GE, ASO-Unigrund-S or ASO-Unigrund-K <br />(mix ratio 1:3 with water). Exclude height differences in the <br />substrate to be laid over and prevent moisture penetration <br />from behind.</p> <p>In areas exposed to moisture, incorporate a fall of at least <br />1.5% in the direction of the drain.</p> <p>2/4</p> <p>04/18</p> <p>Floor drains should have a thin-bed flange of minimum <br />circumferential width of 5 cm and consist of a material <br />suitable for bonding such as e.g. stainless steel, brass, <br />PVC-U. <br />Before tiling heated screeds, they must be commissioned <br />in accordance with recognized technical regulations. <br />Carry out moisture measurements with a carbide <br />hygrometer (CM device) to determine the readiness of a <br />substrate to receive finishes. Moisture measurements may <br />not exceed <br />• CT ≤ 2.0 CM% for screeds on insulation or separating <br />layers <br />• Calcium sulphate screeds without underfloor heating <br />≤ 0.5 CM% <br />• Calcium sulphate screeds with underfloor heating <br />≤ 0.3 CM% <br />The carbide hygromter measurement is to be carried <br />out in accordance with current FBH-AD working <br />practice extracted from the technical information <br />sheet “Coordination of cut-out areas in heated floor <br />construction”. <br />Calcium sulfate screeds can be accepted in privately <br />used bathrooms without a floor drain. They must be <br />abraded, vacuumed and as with all calcium sulfate based <br />substrates primed with ASO-Unigrund-GE, <br />ASO-Unigrund-S or ASO-Unigrund-K (mix ratio 1:3 <br />with water).</p> <p>of 1 mm achieves a dry film thickness of approx. <br />0.6 mm. In wet duty class A, at least two coats are <br />required when brush or roller applying. The previous <br />coat must have dried out before the second coat is <br />applied. <br />3. For the formation of impermeable movement and <br />connecting joints, insert the system components from <br />the ASO-Joint-Tape technology appropriate for the <br />particular wet duty class. Coat both sides of the joint <br />to be bridged with SANIFLEX to at least 2 cm wider <br />than the joint tape, with a 4–6 mm notched trowel. Lay <br />the joint tape into the wet coat and then carefully press <br />into the waterproofing layer with a steel trowel or hard <br />roller, without voids are folds. Ensure that, as far as <br />possible full bedding and full contact is achieved. Bond <br />in such a way as to exclude water migration around <br />the back of the joint tape and pre-formed pieces. <br />Lay the joint tape in a loop over the movement joint. <br />Overlap joint tape ends by a minimum of 5 to 10 cm, <br />bond with SANIFLEX without folds and with a full bed, <br />overcoat and incorporate seamlessly into the surface <br />applied membrane. Insert pre-formed pieces following <br />the same method. Use the named joint tapes and preformed strips as system components. <br />4. Installation of tiles is carried out with one of the named <br />adhesives from the system components. At the time of <br />tiling, the waterproof coat must have hardened. <br />5. Do not expose SANIFLEX to water until cured. In this <br />context, bonded overlapped areas of joint tape/ <br />pre-formed pieces will take considerably longer to dry <br />dependent on ambient conditions.</p> <p>Product Preparation: <br />1. Prime the substrate with ASO-Unigrund-GE, <br />ASO-Unigrund-S or ASO-Unigrund-K (1:3 to 1:4 <br />diluted with water). If a water vapour barrier function is <br />required e.g. in the Scandinavian (timber) construction <br />method, use ASO-Unigrund-D. <br />2. Once the primer has dried, apply SANIFLEX undiluted <br />with a steel float, brush or a lamb’s wool roller. <br />When trowel applying, an even thickness is achieved <br />by using a 4 mm notched trowel and subsequently <br />smoothening. Overcoat any voids. A wet film thickness</p> <p>Important advice: <br />• Protect areas not be treated with SANIFLEX. <br />• Polymer dispersions can only dry out if the temperature <br />of the substrate is at least +3°C above the dew point <br />of the air in the room and there is also air movement. <br />Therefore in rooms with high humidity, plan for longer <br />drying times. If there is a risk of dropping below</p> <p>3/4</p> <p>04/18</p> <p>the dew point (condensation forming), introduce <br />dehumidifiers until the waterproof membrane has cured. <br />• Observe the appropriate relevant technical data sheet <br />for the named products. <br />• Follow relevant current regulations. For e.g. <br />DIN 18157 <br />DIN 18352 <br />DIN 18560 <br />EN 13813 <br />DIN 1055 <br />The BEB information sheets distributed by <br />Bundesverband Estrich und Belad e.V. <br />The technical information “Coordination of cut-out areas <br />in heated floor construction” <br />The ZDB information sheets distributed by the <br />Fachverband des deutschen Fliesenegwerbes: <br /> [*1] „Bonded waterproof membranes” <br /> [*3] „Movement joints in ceramic wall and floor tile <br />finishes” <br /> [*5] „Ceramic tiles and slabs, natural stone and <br />cement bound composite slabs on cement-based <br />floor constructions with insulation.” <br /> [*6] „Ceramic tiles and slabs, natural stone and <br />cement bound composite slabs on heated <br />cementbased floor constructions.” <br />Please observe a current valid EU Safety data sheet. <br />GISCODE: D1</p> <p>Information about the emission level of volatile compounds in indoor <br />air, which pose a health risk by inhalation, on a scale from class A+ <br />(very low emissions) to C (high emissions).</p> <p>This technical data sheet is a translation from German and does not consider local building codes or legal requirements. It shall be used as general reference for the <br />product. Legally binding is only the latest German technical data sheet or the latest data sheet from one of our foreign subsidiaries inside their sales territory. <br />4/4</p> <p>WKD/CoS/TM</p> <p>04/18</p>
